Welding flux->Fused Welding Fluxes->JN-HJ431JN-HJ431Description: HJ431 is a kind of smelting-type, red brown to light yellow colored, glassy granulated flux with high manganese and silicon but low fluorine, mesh of 8-40(2.5-0.45mm) and...
Welding flux. Fluorine alkali type sintering flux. Basicity about 1.8, spherical shape particles size, 10-60. Excellent Welding performance, stable arc burning, slag, weld moulding beauty to weld high low-temperature impact toughness, ac, dc Welding...
Flux LJ-SJ501 ( F7A0-EL12 .F7A0-EM12K)Explanation: LJ-SJ501 is a kind of aluminum-titanium type acidity agglomerated flux, with alkalinity around 0.5 ~ 0.8. They are gray and round grain, with grain size around 2.0 ~ 0.28mm. It can be operated with...
Product Name:Gas Welding Flux & Brazing Flux
1.UsageAtomised ferrosilicon 45% is used extensively in the Welding industry.2.Sizes-250um 100%passing-149um 90-100%passing-105um 70-80% passing-74um 40-50%passing-63um 30-40%passing-45um 10-20%passing(or we can make any size according to the...
...
ZINC AMMONIUM CHLOIRDE used in metal Welding and used as material of dry cell.Zinc Ammonium Chloride Galvanizing FluxZinc Ammonium Chloride based Proprietary Galvanizing Flux in Powder form for Wet Flux applications ( LOW FUMING and COST EFFECTIVE...
GOOT/BS-10 solder paste, solder aid and strong, bright solder joints, residual low. The flux is stable, volatile small, cycle length, amount of provincial, non-toxic, odorless, safe and reliable operation, is to create high-quality electronic...
Estweld exothermic power /Thermit Welding
Welding flux: HJ330Conforming to GB/T12470 F48A0-H10Mn2Equivalent to JIS YSF-W41Description: HJ330 is defined as fused type Fluxes low medium manganese, high silicate and low fluorine elements, color in brown with vitreous granules 8-40 meshes in...
Silver brazing alloy Welding of copper and copper alloy steel and stainless steel, metal brazing, heterogeneous with silicon aluminum brazing alloy aluminum, aluminum brazing manganese etc
Silver paste, silver solder, solder paste, fluxQJ305 paste silver brazing solvent is a successful development of our latest set of various domestic and international advantages of the new silver brazing flux solvent, its fluidity, permeability are...
NameProducerClassStandardHardnessMaterial IdentificationARCFCWBeijing ARCtopGB10045-88HRC58-65High chromium, high carbon iron-based alloyChemical CompositionCCrMnSiotherscontent5.528++<5
AWS A5.17 F6A0-EL12 (SJ301) is a kind of silicon-calcium type Welding electrode, the alkalinity is 1.01.Size: 10-60Mesh2.Stable Welding arc 3.good slag detachability4.good weld appearance5.Suitable for DC and AC current6.it matches with EL12,EM12,...
Exothermic Welding Flux:The capacity of an earthing circuit to protect the safety of personnel depends on the quality of the connections made .SHENTONG exothermic Welding is RENTONG ' s patent product in China . And it has the best quality in China...
Brazing flux is used to provide active and remove oxide on work pieces and brazing filler metal.Brazing flux is used to provide active and remove oxide on work pieces and brazing filler metal, and facilitate the shaping of brazing joint. It helps...
Description:SJ101G It is a special-purpose sintered flux developed especially for Welding steel pipes that are used in the project of Transporting the Natural Gas from the West to the Easti. The Welding wire is connected to the posiitive electrode...
Advantages:1.Current carrying capability from Welding point is same as conductor with good conducting performance. After inspection, the DC resistance ratio and change rate are almost zero before and after Welding. This is the level that any of the...
Agglomerated Submerged Arc Welding Flux DIAMOND 101Classifications GB F4A4-H08MnA F5A4-H10Mn2AAWS F7A4-EH14JIS S502-HGeneral CharacteristicsType: fluoride-alkaline type slag serialBasicity: 1.6-1.8Grain Size: 10-60 meshes(2.0-0.28mm)Color:...
1. Commodity: Welding flux 2. Type : AWS A5.17: F6A0-EL8(SJ401)3. Grain size: 2.00-0.28mm (10-60mesh)4. Typical Flux Composition Range:SiO2+TiO2:35-45%, CaO+MgO:5-15%, Al2O3+MnO:40-50%, CaF2:<15% 5. Typical weld metal mechanical properties:Yield...